Koattro KT AR05

About
Koattro KT AR05 is a novel plastomeric material based on LyondellBasell technology with unique characteristics. The product shows an excellent compression set performance which is highly compatible with Polypropylene. Blended with PP it enhances softness, elastic recovery, elongation at break and impact resistance whilst improving transparancy and reducing stress whitening. Blended at low concentrations in PP, Koattro KT AR05 enhances also the thermal bonding strength. KT AR05 is available in free flowing pellet form. This product is not intended for use in medical and pharmaceutical applications.&&

About

Koattro KT AR05 is a novel plastomeric material based on LyondellBasell technology with unique characteristics. The product shows an excellent compression set performance which is highly compatible with Polypropylene. Blended with PP it enhances softness, elastic recovery, elongation at break and impact resistance whilst improving transparancy and reducing stress whitening. Blended at low concentrations in PP, Koattro KT AR05 enhances also the thermal bonding strength. KT AR05 is available in free flowing pellet form. This product is not intended for use in medical and pharmaceutical applications.&&

Product Description
Supplier	LyondellBasell
Generic	乙烯基辛烯塑料
Material Status	Commercial: Active
Features	Excellent Processability,High elastic,Foaming performance,Good melt strength,Low temperature toughness,Moderate liquidity,Welding
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.890	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	0.50	g/10min	ISO 1133

elastic body	Nominal value	Unit	Test method
Compression deformation
70℃	42	%	ASTM D395B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180
-20℃	5.1	kJ/m²	ISO 180
0℃	无断裂		ISO 180
23℃	无断裂		ISO 180

THERMAL	Nominal value	Unit	Test method
Melting temperature	114	℃	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	87		ISO 868
Tensile modulus	19.0	MPa	ISO 527-2
tensile strength
Fracture, molded	12.0	MPa	ISO 8986-2
Tensile strain
Fracture, molded	> 400	%	ISO 8986-2
Bending modulus
23℃	25.0	MPa	ISO 178

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	200 to 260	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.