| About |
|---|
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low odor,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 10 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 2.0 | % | ISO 294 |
| Water absorption rate | |||
| 23℃，24hr | 0.22 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 95 | ℃ | ISO 75 |
| Melting temperature | 170 | ℃ | ISO 3146 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.8mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 64.0 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 35 | % | ISO 527-1/2 |
| Bending modulus | |||
| 23℃ | 2750 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 86 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 80 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| Processing temperature | Nominal value | Unit | Test method |
| drying temperature | 80-120 | ℃ | |
| Drying time | 3 | hrs | |
| Temperature at the rear of the barrel | 160-180 | ℃ | |
| Temperature in the middle of the barrel | 190-200 | ℃ | |
| Front temperature of material barrel | 190-200 | ℃ | |
| Mold temperature | 60-80 | ℃ | |
| Maximum processing temperature | 220 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |