| About |
|---|
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Medium Viscosity,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Filling material content | |||
| 190 ℃, 2.16 kg | 15.0 | g/10min | ISO 1133 |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 12.5 | cm³/10min | ISO 1133 |
| Shrinkage rate | 1.8-2.2 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.22 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.5 | kJ/m² | ISO 179/1eA |
| -30℃ | – | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | |||
| 20 ℃/min | 173 | ℃ | ISO 11357-1 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 95 | ℃ | ISO 75 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 4 mm，50 mm/min | 67 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 50 mm/min | 30 | % | ISO 527 |
| Yield, 50 mm/min | 10 | % | ISO 527 |
| Bending modulus | |||
| 2 mm/mim | 2,800 | MPa | ISO 178 |
| bending strength | |||
| 2 mm/min | 88 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 82 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Temperature limit | 200 | ℃ | |
| Control moisture content | ≤ 0.1 | % | |
| drying temperature | 80 ~ 90 | °C | |
| Drying time | 3-5 | hr | |
| Temperature at the rear of the barrel | 160-180 | °C | |
| Temperature in the middle of the barrel | 170-190 | °C | |
| Front temperature of material barrel | 180-200 | °C | |
| Nozzle temperature | 180-200 | °C | |
| Mold temperature | 60-80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |