| About |
|---|
| KOPA® KN133G30BL is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant Medium Viscosity&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 , ISO 1183 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 60% RH | 0.40 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 205 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 193 | ℃ | ISO 75-2/A |
| Melting peak temperature | 220 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD | 3.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 21 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.60 | ASTM D150 | |
| Arc resistance | 130 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | |||
| 23℃ | 172 | MPa | ASTM D638 |
| 23℃ | 170 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 8.5 | % | ASTM D638 |
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8430 | MPa | ASTM D790 |
| 23℃ | 7400 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 275 | MPa | ASTM D790 |
| 23℃ | 240 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 to 100 | °C | |
| Drying time – hot air dryer | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 230 | °C | |
| Barrel middle temperature | 245 | °C | |
| Barrel front temperature | 250 | °C | |
| Nozzle temperature | 255 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |