| KOPA® KN3321G10V0Y is a Polyamide 66 (Nylon 66) product filled with glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant Flame Retardant Good Dimensional Stability Good Toughness&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good Dimensional Stability,Flame Characteristics |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 110 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 150 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 4,850 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 205 | ℃ | ISO 75-2/A |
| Melting temperature | 255 | ℃ | ISO 11357-3 |
| Vicat Softening Temp |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+9 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 9 | KV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.40mm | V-0 | UL 94 | |
| 0.80mm | V-0 | UL 94 | |
| 1.50mm | V-0 | UL 94 | |
| 3.00mm | V-0 | UL 94 | |
| Igniting temperature of the hot wire | |||
| 0.8 mm | 825 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 825 | ℃ | IEC 60695-2-12 |
| 3 mm | 800 | ℃ | IEC 60695-2-12 |
| Relative temperature of heating wire | |||
| 0.80mm | 960 | ℃ | IEC 60695-2-13 |
| 1.50mm | 960 | ℃ | IEC 60695-2-13 |
| 3.00mm | 960 | ℃ | IEC 60695-2-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 -100 | °C | |
| Drying time | 4-5 | Hr | |
| Water content | ≤0.05 | % | |
| Injection temperature | |||
| Rear barrel temperature | 260 | °C | |
| Central temperature of the barrel | 265 | °C | |
| Barrel front temperature | 270 | °C | |
| Mold temperature | 60-80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |