| About |
|---|
| KOPA® KN333G30CRN is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant Chemical Resistant&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | HB,Grease resistance |
| Availabilitys | Asia Pacific,Latin America,Europe,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific gravity | 1.36 | ASTM D792 | |
| Shrinkage rate | |||
| Parallel | 0.2-0.4 | % | ASTM D955 |
| Normal | 0.9-1.1 | % | ASTM D955 |
| Water absorption | |||
| 23℃，24 hr | 1 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact Strength | |||
| 23℃ | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 255 | ℃ | ASTM D648 |
| Melting point | 260 | ℃ | ASTM D1525 |
| Coefficient of linear thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.8 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength | |||
| 5mm/min | 180 | MPa | ASTM D638 |
| Flexural modulus | |||
| 5mm/min | 8900 | MPa | ASTM D790 |
| Flexural strength | |||
| 5mm/min | 300 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 120 | R Scale | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying Temperature | 80 to 90 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content Processing Moisture Content | < 0.1 | % | |
| Rear Temperature of Material Barrel | 270-285 | °C | |
| Middle Temperature in the middle of the barrel | 280-300 | °C | |
| Front Temperature of Material Barrel | 285-305 | °C | |
| Nozzle Temperature | 285-305 | °C | |
| Mold Temperature | 70 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |