| KOPA® KN333G35CR是一种聚酰胺66（尼龙66）产品,含有的填充物为35% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在亚太地区、北美洲、拉丁美洲或欧洲有供货。 典型应用领域为:汽车行业。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 耐候性好 耐热 良好的尺寸稳定性&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Dimensional Stability,High Heat Resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 60% RH | 0.40 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 248 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 245 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 250 | ℃ | ASTM D648 |
| Melting peak temperature | 255 | ℃ | ASTM D1525 |
| Melting temperature | 255 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 21 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.60 | ASTM D150 | |
| Arc resistance | 135 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 190 | MPa | ISO 527-2 |
| 23℃ | 186 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Fracture, 23 ℃ | 7.5 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 8830 | MPa | ASTM D790 |
| 23℃ | 8800 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 284 | MPa | ASTM D790 |
| 23℃ | 265 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 to 100 | °C | |
| Drying time – hot air dryer | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 260 | °C | |
| Barrel middle temperature | 275 | °C | |
| Barrel front temperature | 280 | °C | |
| Nozzle temperature | 285 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |