KOPELEN J-330S

About
Description J-330S is impact block copolymer which has ethylene-propylene rubber inside homo polypropylene. This grade can be processed by extrusion and thermoforming. J-330S shows good impact resistance at low temperature and high strength. It has good vacuum molding property, suitable for the production of vacuum molding goods. J-330S is mainly applied to straw for drinking. Applications Straw for drinking Vacuum forming use Blow molding goods&&

About

Description J-330S is impact block copolymer which has ethylene-propylene rubber inside homo polypropylene. This grade can be processed by extrusion and thermoforming. J-330S shows good impact resistance at low temperature and high strength. It has good vacuum molding property, suitable for the production of vacuum molding goods. J-330S is mainly applied to straw for drinking. Applications Straw for drinking Vacuum forming use Blow molding goods&&

Product Description
Supplier	LOTTE
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Block Copolymer,low-temperature impact resistance,HB
Availabilitys	North America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D792 , ISO 1183
Melt Flow Rate
230℃，2.16kg	4.0	g/10min	ASTM D1238，ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	27.5	MPa	ASTM D638
yield	26.0	MPa	ISO 527-2
Tensile strain
fracture	> 100	%	ASTM D638 , ISO 527-2
Bending modulus
—	1270	MPa	ASTM D790
—	1080	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-10℃	29	J/m	ASTM D256
-10℃	25	J/m	ISO 180
23℃	89	J/m	ASTM D256
23℃	78	J/m	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	105	℃	ASTM D648
0.45 MPa, unannealed	85.0	℃	ISO 75-2/B

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.