| KOPLA PA6 KNX1014是一种聚酰胺6（尼龙6）材料,含有的填充物为20% 玻璃矿物。 该产品在亚太地区有供货,。 KOPLA PA6 KNX1014的主要特性有: 阻燃/额定火焰 坚硬 良好的尺寸稳定性 KOPLA PA6 KNX1014的典型应用领域为:汽车行业 |
| Product Description | |
|---|---|
| Supplier | KOPLA |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.60 to 0.80 | % | |
| TD：3.0 mm | 0.70 to 1.0 | % | |
| Water absorption rate | |||
| 23℃，24hr | 1.2 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.00 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | |
| 1.8 MPa, unannealed | 200 | ℃ | |
| Melting temperature | 222 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 22 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.50 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.020 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| Tensile modulus | |||
| 23℃ | 5500 | MPa | ASTM D638 |
| Tensile strength (23 ° C) | 100 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 4800 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 160 | MPa | ASTM D790 |
| Poisson’s ratio (23 ° C) | 0.35 | ASTM D638 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |