| KOPLA PA66 KDCL1030是一种聚酰胺66（尼龙66）材料,含有的填充物为30% 碳纤维增强材料。 该产品在亚太地区有供货,。 KOPLA PA66 KDCL1030的主要特性有: 阻燃/额定火焰 坚硬 抗蠕变 耐冲击 典型应用领域包括: 电气/电子应用 汽车行业 体育用品 |
| Product Description | |
|---|---|
| Supplier | KOPLA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.30 to 0.80 | % | ASTM D955 |
| TD：3.0 mm | 0.30 to 0.80 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 58 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 11.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 245 | ℃ | ASTM D648 |
| Melting temperature | 262 | ℃ | DSC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| R-level | 122 | ISO 2039-2 | |
| Tensile modulus | |||
| 23℃ | 24100 | MPa | ASTM D638 |
| Tensile strength | |||
| 23°C | 255 | MPa | ASTM D638 |
| 23°C | 312 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 19300 | MPa | ASTM D790 |
| 23℃ | 19000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 350 | MPa | ASTM D790 |
| 23℃ | 400 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |