| KOPLA PA66 KDG1030ST is a Polyamide 66 (Nylon 66) material filled with 30% glass fiber. It is available in Asia Pacific. Important attributes of KOPLA PA66 KDG1030ST are: Flame Rated Chemical Resistant Clarity High Strength Rigid Typical applications include: Automotive Electrical/Electronic Applications Furniture&& |
| Product Description | |
|---|---|
| Supplier | KOPLA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Clarity,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.80 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 160 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 255 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 250 | ℃ | ASTM D648 |
| Melting temperature | 260 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 3.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 25 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| tensile strength | |||
| Yield, 23 ℃ | 186 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 9410 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 265 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |