| About |
|---|
| KOPLA PA66 KDP1000R是一种聚酰胺66（尼龙66）材料,。 该产品在亚太地区有供货,加工方式为:注射成型。 KOPLA PA66 KDP1000R的主要特性有: 阻燃/额定火焰 耐冲击 典型应用领域包括: 电气/电子应用 工程/工业配件 汽车行业 |
| Product Description | |
|---|---|
| Supplier | KOPLA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | |
| Shrinkage rate | |||
| MD：3.0 mm | 1.5 to 2.0 | % | |
| TD：3.0 mm | 1.8 to 2.2 | % | |
| TD：3.0 mm | 1.5 to 2.0 | % | |
| Water absorption rate | |||
| 23℃，24hr | 1.3 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | |
| Charpy Unnotch Impact strength | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.00 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | |
| 1.8 MPa, unannealed | 90.0 | ℃ | |
| Melting temperature | 263 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | |
| Dielectric strength | 27 | kV/mm | |
| Dielectric constant | |||
| 1 MHz | 2.90 | ||
| Dissipation factor | |||
| 1 MHz | 0.030 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ||
| Tensile modulus | |||
| 23℃ | 3200 | MPa | |
| Tensile strength (23 ° C) | 83.0 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 30 | % | |
| Bending modulus | |||
| 23℃ | 3000 | MPa | |
| bending strength | |||
| 23℃ | 120 | MPa |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |