| KOPLA PP KPL1060是一种聚丙烯材料,含有的填充物为60% 长玻璃纤维。 该产品在亚太地区有供货,。 KOPLA PP KPL1060的主要特性有: 阻燃/额定火焰 坚硬 抗蠕变 耐冲击 KOPLA PP KPL1060的典型应用领域为:汽车行业 |
| Product Description | |
|---|---|
| Supplier | KOPLA |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,low-temperature impact resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.10 to 0.40 | % | ASTM D955 |
| TD：3.0 mm | 0.10 to 0.40 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 42 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 82 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 30.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 165 | ℃ | ASTM D648 |
| Melting temperature | 165 | ℃ | DSC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| R-level | 110 | ISO 2039-2 | |
| Tensile modulus | |||
| 23℃ | 13500 | MPa | ASTM D638 |
| 23℃ | 12500 | MPa | ISO 527-2 |
| Tensile strength | |||
| 23°C | 180 | MPa | ASTM D638 |
| 23°C | 155 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.5 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 12000 | MPa | ASTM D790 |
| 23℃ | 13600 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 220 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |