KPOL-PP K-PPC 1.50

About
Polypropylene Heterophasic Copolymer Characteristics The KPOL® resin is a propylene impact copolymer designed for injection molding applications, Excellent Balance of Stiffness and Impact Strength at low temperatures, Contains Nucleating , Good Mold Release. Superior Drop Impact at Refrigeration Temperature, Very High Flexural Modulus. Also is suitable for technical components: toys, sports, equipment, leisure goods, automotive, pallets, crates and pails. Applications Injection / Automobile applications, Battery case, Home appliances, Industrial parts for electronic. Thermoformed packages with high impact strength; Blown packages and technical parts in general; sheet extrusion.&&

About

Polypropylene Heterophasic Copolymer Characteristics The KPOL® resin is a propylene impact copolymer designed for injection molding applications, Excellent Balance of Stiffness and Impact Strength at low temperatures, Contains Nucleating , Good Mold Release. Superior Drop Impact at Refrigeration Temperature, Very High Flexural Modulus. Also is suitable for technical components: toys, sports, equipment, leisure goods, automotive, pallets, crates and pails. Applications Injection / Automobile applications, Battery case, Home appliances, Industrial parts for electronic. Thermoformed packages with high impact strength; Blown packages and technical parts in general; sheet extrusion.&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Antifreeze,Nucleation,Good stripping performance,Inoxidizability,Impact copolymer
Availabilitys	North America,Latin America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D1505
Melt Flow Rate
230℃，2.16kg	1.5	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-20℃	50	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	88.0	℃	ASTM D648
Vicat Softening Temp	150	℃	ASTM D1525 3

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	78		ASTM D785
tensile strength
yield	25.0	MPa	ASTM D638
Tensile strain
fracture	10	%	ASTM D638
Bending modulus
1% secant	1200	MPa	ASTM D790

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.