| About |
|---|
| Kraton D1101 K is a clear, linear triblock copolymer based on styrene and butadiene with a polystyrene content of 31%. It is supplied from North America in the physical form identified below. Kraton D1101 KT – supplied as a dusted porous pellet Kraton D1101 KU – supplied as an undusted porous pellet Kraton D1101 KIM – supplied as a dusted powder Kraton D1101 K is used as a modifier of bitumen or thermoplastics and in compound formulations. It may also find use as an ingredient in formulating adhesives, sealants and coatings.&& |
| Product Description | |
|---|---|
| Generic | SBS |
| Material Status | Commercial: Active |
| Features | Inoxidizability,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D4025 |
| Melt Flow Rate | |||
| 200℃，5.0kg | < 1.0 | g/10min | |
| Antioxidant Additive | 0.15 to 0.40 | % | Internal Method |
| Polystyrene content | 29 to 33 | % | Internal Method |
| Total Extractables | < 1.0 | % | Internal Method |
| Ash Content | |||
| KIM | 4.0 to 6.0 | % | |
| KT | 0.2 to 0.4 | % | Internal Method |
| Volatiles | < 0.70 | % | Internal Method |
| Solution viscosity | |||
| 25wt% toluene, 25 ℃ | 3.9 | Pa·s | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw A, 10 seconds, molded | 69 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 31.7 | MPa | ASTM D412 |
| 300% strain | 2.76 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 880 | % | ASTM D412 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Diblock Content | 16.0 | ||
| Styrene/Rubber ratio | 31/69 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 25%w toluene solution at 25°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |