| HDPE KS 10100 UE 聚乙烯树脂是一种高密度聚乙烯树脂，加工性能有所提升，应用于室外环境时，抗冲击强度、应力开裂性能和紫外线稳定性均优异，而且可以将翘曲降低至最低水平。 |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,High ESCR |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.955 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| 190℃，5.0kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：250℃ | 2.6 | % | ASTM D955 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 100% emulsifier, molded | 10.0 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | |||
| Compression Molding | 85.0 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 128 | ℃ | ISO 306/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 65 | ISO 868 | |
| tensile strength | |||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Fracture, molded | 27.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | > 1600 | % | ASTM D638 |
| Bending modulus | |||
| 2% cut, molded | 850 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |