| About |
|---|
| ABS BM510 is a high impact ABS resin for blow molding. Application:automobile rear spoiler, side step, car seat, fiber reinforced plastic jar inner liner.&& |
| Product Description | |
|---|---|
| Supplier | KumhoSunny |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 23℃ | 0.40 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 15 | kJ/m² | ISO 179 |
| 23℃ | 33 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 32 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 95.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 106 | ISO 2039-2 | |
| tensile strength | 45.0 | MPa | ISO 527-2/50 |
| Bending modulus | 2200 | MPa | ISO 178 |
| bending strength | 65.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 170 to 190 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 190 to 220 | °C | |
| Nozzle temperature | 180 to 210 | °C | |
| Processing (melt) temperature | 180 to 220 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Back pressure | 1.00 to 5.00 | MPa | |
| Screw speed | 30 to 70 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Condition: 4 J |
| 4. Condition: 5.5 J |
| 5. 120°C/h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |