| About |
|---|
| HAM8541H is paint free improved PMMA/ABS resin.HAM8541H has comprehensive properties:(1)anti-scratch,PH=2H (2) high gloss(G60°>95)(3)free style(black and spark,semitransparent,spark,transparent) (4)cheap.HAM8541H is mainly used in complex part, thin layer part ,small appliance as telephone, sound. etc.&& |
| Product Description | |
|---|---|
| Supplier | KumhoSunny |
| Generic | ABS+PMMA |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High scratch resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 20 | % | ASTM D638 |
| Bending modulus | 2500 | MPa | ASTM D790 |
| bending strength | 75.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 70 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 86.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 96.0 | ℃ | ASTM D1525 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 220 to 230 | °C | |
| Barrel front temperature | 230 to 240 | °C | |
| Nozzle temperature | 225 to 235 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Back pressure | 1.00 to 5.00 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |