| About |
|---|
| HSP8340GNH is non-halogen high gloss PS/PPO resin. HSP8340GNH has excellent creep performance in low and high temperature, low water absorption,high flow and high shape resistance property. HSP8340GNH is mainly used in electron & electric parts, OA appliance, fluid engineering,etc.&& |
| Product Description | |
|---|---|
| Supplier | KumhoSunny |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good surface appearance,High liquidity,Low or no water absorption,Halogen free,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 40 to 60 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 52.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 15 | % | ASTM D638 |
| Bending modulus | 2380 | MPa | ASTM D790 |
| bending strength | 78.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 190 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 90.0 | ℃ | ASTM D1525 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| CSA File No. | LS 66457 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 240 to 250 | °C | |
| Barrel front temperature | 250 to 265 | °C | |
| Nozzle temperature | 250 to 260 | °C | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Back pressure | 0.200 to 0.800 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |