| About |
|---|
| HSP8340NH is non-halogen general purpose PS/PPO resin. HSP8340NH has excellent creep performance in low and high temperature, high rigidity,low water absorption and high shape resistance property. HSP8340NH is mainly used in electron & electric parts, OA appliance, fluid engineering,etc.&& |
| Product Description | |
|---|---|
| Supplier | KumhoSunny |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low or no water absorption,Halogen free,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 50 to 65 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 42.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 35 | % | ASTM D638 |
| Bending modulus | 2110 | MPa | ASTM D790 |
| bending strength | 62.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 340 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 78.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 88.0 | ℃ | ASTM D1525 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| CSA File No. | LS 66457 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 240 to 250 | °C | |
| Barrel front temperature | 250 to 260 | °C | |
| Nozzle temperature | 250 to 255 | °C | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Back pressure | 0.200 to 0.800 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |