| KYDEX® V sheet is a recycled grade of a proprietary thermoplastic sheet that is cost competitive with other grades of thermoplastic sheet while offering improved performance.&& |
| Product Description | |
|---|---|
| Supplier | Sekisui |
| Generic | PMMA+PVC |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Sprayable,Machinable |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 430 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.18 mm | 73.9 | ℃ | ASTM D648 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Temperature of hot forming mold | 163 to 200 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.18 mm | 88 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.18 mm | 42.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 3.18 mm | 2310 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.18 mm | 63.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Male Mold |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |