KYDEX® XD - SOLIAO

About
KYDEX® XD is a thermoplastic 3D laminate giving designers the ability to incorporate compound corners, logos, and wire management holes while eliminating unsightly seams and the need for edgebanding typically associated with HPL/TFM surfaces. Its integral color and superior impact resistance minimizes costly mainenance associated with other laminates. Extreme durability (XD), superior impact, membrane pressable thermoplastic 3D laminate with integral color from 0.76mm-1.02mm (0.030″-0.040″) thickness. While providing good definition it surpasses vinyl overlays, high pressure laminates and melamine in resistance to surface and edge impact.&&

About

KYDEX® XD is a thermoplastic 3D laminate giving designers the ability to incorporate compound corners, logos, and wire management holes while eliminating unsightly seams and the need for edgebanding typically associated with HPL/TFM surfaces. Its integral color and superior impact resistance minimizes costly mainenance associated with other laminates. Extreme durability (XD), superior impact, membrane pressable thermoplastic 3D laminate with integral color from 0.76mm-1.02mm (0.030″-0.040″) thickness. While providing good definition it surpasses vinyl overlays, high pressure laminates and melamine in resistance to surface and edge impact.&&

Product Description
Supplier	Sekisui
Generic	PMMA+PVC
Material Status	Commercial: Active
Features	Excellent Processability,Good flexibility,High impact resistance,Flame Characteristics,Good wear resistance,Durability,High scratch resistance,Low moisture absorption
Availabilitys	North America,Latin America,Asia Pacific,Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ASTM D792

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
1.02mm	800	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
1.8 MPa, unannealed	66.2	℃	ASTM D648
1.8 MPa, annealed, 3.18 mm	75.6	℃	ASTM D648

Supplementary information	Nominal value	Test method
Falling ball impact test
1.02 mm	> 3000	Internal Method
Cleanability	16.0	Internal Method
Drop hammer impact
1 mm	> 1000	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-grade, 3.18 mm	94		ASTM D785
Tensile modulus
3.18 mm	2420	MPa	ASTM D638
tensile strength
3.18 mm	42.0	MPa	ASTM D638
Tensile strain
Fracture, 3.18 mm	130	%	ASTM D638
Bending modulus
3.18 mm	2480	MPa	ASTM D790
bending strength
3.18 mm	66.0	MPa	ASTM D790
Taber abraser
1000 cycles, 500 g, CS-10F wheel	0.00950	mg	ASTM D1044

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.