| About |
|---|
| Product Description | |
|---|---|
| Supplier | Arkema |
| Material Status | Commercial: Active |
| Features | Hypocrystalline |
| Availabilitys | Europe,Africa & Middle East ,Latin America,Asia Pacific,North America |
| Process Methods | Injection Molding,Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water Absorption | 0.03 | % | ISO 62 |
| Moisture Absorption | 0.015 | % | ISO 62 |
| Density | 1780 | kg/m³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，5kg | 1.1 | cm³/10min | ISO 1133 |
| Molding shrinkage | |||
| Parallel | 2.0 | % | ISO 294-4 |
| Normal | 2.0 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527 |
| Tensile Strength | |||
| Yield yld | 50 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield yld | 7 | % | ISO 527 |
| Broken BRK | >50 | % | ISO 527 |
| Tensile creep modulus | |||
| 1h | 1050 | MPa | ISO 899-1 |
| 1000h | 570 | MPa | ISO 899-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 244 | kJ/m² | ISO 179/1eU |
| -30℃ | 186 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| -30℃ | 5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 168 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | -40 | ℃ | ISO 11357-2 |
| Hot deformation temperature HDT | |||
| 1.80 MPa | 105 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 135 | ℃ | ISO 75-1/-2 |
| Vicat Softening Temperature | 135 | ℃ | ISO 306/B |
| Coeff. of linear thermal expansion | |||
| Parallel | 150 | E-6/K | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.6 mm | V-0 | calss | IEC 60695-11-10 |
| 0.8 mm | V-0 | calss | IEC 60695-11-10 |
| Oxygen Index | 43 | % | ISO 4589-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100Hz | 11 | IEC 60250 | |
| 1MHz | 8 | IEC 60250 | |
| Dissipation Factor | |||
| 100Hz | 260 | E-4 | IEC 60250 |
| 1MHz | 2310 | E-4 | IEC 60250 |
| Volume Resistance | 2E12 | ohm·m | IEC 60093 |
| Surface Resistivity | >1E15 | ohm | IEC 60093 |
| Electric strength | 21 | kV/mm | IEC 60243-1 |
| Compared Tracking Index | 600 | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Melt Temperature | 210 | ℃ | |
| Mold Temperature | 90 | ℃ | |
| Injection speed | 10 | mm/s | |
| Maintain pressure at hold | 13 | MPa | |
| Forming temperature | 225 | ℃ | |
| Forming time | 3 | ℃ | |
| Demolding temperature | 120 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |