| LACEA® H-100J (Stretched)是一种聚乳酸 (PLA)材料,。 该产品在亚太地区有供货,加工方式为:吹塑薄膜或注射成型。 LACEA® H-100J (Stretched)的主要特性为:环保/绿色。 典型应用领域包括: 包袋/内衬 包装 电影 容器 无纺布&& |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Biodegradable |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D1505 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| MD | 3850 | MPa | ASTM D882 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| MD, fracture | 140 | % | ASTM D882 |
| Elmandorf tear strength | |||
| TD | 2.7 | g | ASTM D1922 |
| Water vapor permeability | 160 | g/m²/24 hr | ASTM E96 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 29 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 55.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 58.0 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 25 µm | 93 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| Level L | 84 | ||
| R-level | 115 | ||
| tensile strength | 68.0 | MPa | ASTM D638 |
| MD, yield | 105 | MPa | ASTM D882 |
| Bending modulus | 3700 | MPa | ASTM D790 |
| bending strength | 98.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 150 to 160 | °C | |
| Barrel middle temperature | 160 to 180 | °C | |
| Barrel front temperature | 170 to 190 | °C | |
| Nozzle temperature | 160 to 180 | °C | |
| Mold temperature | 20.0 to 30.0 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |