| About |
|---|
| LAPEROS® E473i是一种液晶聚合物（LCP）产品,含有的填充物为30% 玻璃矿物。 它,在亚太地区有供货。 特性包括: 阻燃/额定火焰 抗翘曲 高流动性&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Low warping,High liquidity,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD：1.00 mm | 0.39 | % | |
| MD：1.0 mm | 0.030 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.020 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 275 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 1 mm | 53 | kV/mm | |
| 3 mm | 26 | kV/mm | |
| Dielectric constant | IEC 60250 | ||
| 1 kHz | 4.20 | ||
| 1 MHz | 3.70 | ||
| Dissipation factor | IEC 60250 | ||
| 1 kHz | 0.020 | ||
| 1 MHz | 0.030 | ||
| Arc resistance | 151 | sec | |
| Compared to the leakage tracing index | 150 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Color Number | VF2201/BK210P |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 55 | ISO 2039-2 | |
| tensile strength | 125 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.8 | % | ASTM D638 |
| Bending modulus | 11000 | MPa | ISO 178 |
| bending strength | 160 | MPa | ISO 178 |
| Bending strain | 2.8 | % | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |