| About |
|---|
| SERIES 60 AND 2103 ETHER Products based on quality polyether. ln comparison with the Ester Series, they show a better resistance to hydrolysis and microbiological attack, a very good cold flexibility but a lower resistance to oxidation.&& |
| Product Description | |
|---|---|
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low temperature toughness,Good wear resistance,Solvent resistance |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | DIN 53479 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | DIN 53504 | ||
| fracture | 61.7 | MPa | DIN 53504 |
| 50% strain | 16.4 | MPa | DIN 53504 |
| 100% strain | 20.8 | MPa | DIN 53504 |
| 300% strain | 45.4 | MPa | DIN 53504 |
| Tensile strain | |||
| fracture | 410 | % | DIN 53504 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| -20℃ | 10.5 | kJ/m² | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 56 | DIN 53505 | |
| Bending modulus | 170 | MPa | ISO 178 |
| Torsional modulus | |||
| -20℃ | 205 | MPa | DIN 53447 |
| 20℃ | 40.0 | MPa | DIN 53447 |
| Ratio（-20℃/+20℃） | 5.10 | ||
| Wear amount | 35.0 | mm³ | DIN 53516 |
| Tear resistance | 140 | MPa | DIN 53515 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |