| About |
|---|
| Polyetheretherketone (PEEK). Unfilled. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.&& |
| Product Description | |
|---|---|
| Supplier | LATI |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Halogen free,High Heat Resistance,Solvent resistance,V-1,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 0.90 to 1.3 | % | ISO 294-4 |
| MD：2.0 mm | 0.80 to 1.2 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.080 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | ||
| 23℃ | 3700 | MPa | ISO 527-1-2 |
| 60℃ | 3700 | MPa | ISO 527-1-2 |
| 90℃ | 3600 | MPa | ISO 527-1-2 |
| 120℃ | 3600 | MPa | ISO 527-1-2 |
| 150℃ | 3200 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/5 | ||
| Yield, 23 ℃ | 105 | MPa | ISO 527-2/5 |
| Yield, 60 ℃ | 85.0 | MPa | ISO 527-2/5 |
| Yield, 90 ℃ | 65.0 | MPa | ISO 527-2/5 |
| Yield, 120 ℃ | 55.0 | MPa | ISO 527-2/5 |
| Yield, 150 ℃ | 25.0 | MPa | ISO 527-2/5 |
| tensile strength | ISO 527-2/5 | ||
| Fracture, 23 ℃ | 90.0 | MPa | ISO 527-2/5 |
| Fracture, 60 ℃ | 80.0 | MPa | ISO 527-2/5 |
| Fracture, 90 ℃ | 65.0 | MPa | ISO 527-2/5 |
| Fracture, 120 ℃ | 55.0 | MPa | ISO 527-2/5 |
| Fracture, 150 ℃ | 25.0 | MPa | ISO 527-2/5 |
| Tensile strain | ISO 527-2/5 | ||
| Yield, 23 ℃ | 5.0 | % | ISO 527-2/5 |
| Yield, 60 ℃ | 5.0 | % | ISO 527-2/5 |
| Yield, 90 ℃ | 5.0 | % | ISO 527-2/5 |
| Yield, 120 ℃ | 6.0 | % | ISO 527-2/5 |
| Yield, 150 ℃ | 8.0 | % | ISO 527-2/5 |
| Tensile strain | ISO 527-2/5 | ||
| Fracture, 23 ℃ | 30 | % | ISO 527-2/5 |
| Fracture, 60 ℃ | 30 | % | ISO 527-2/5 |
| Fracture, 90 ℃ | 30 | % | ISO 527-2/5 |
| Fracture, 120 ℃ | 35 | % | ISO 527-2/5 |
| Fracture, 150 ℃ | 45 | % | ISO 527-2/5 |
| friction coefficient | ASTM D1894 | ||
| dynamic | 0.26 | ASTM D1894 | |
| static state | 0.32 | ASTM D1894 | |
| Wear factor | 1.50E-6 | mm³/Nm | ASTM D3702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | No Break | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 165 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 195 | ℃ | ISO 75-2/B |
| Continuous use temperature | 210 | ℃ | |
| Vicat Softening Temp | |||
| B50 | > 300 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：30~100℃ | 6.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-1 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 875 | ℃ | IEC 60695-2-13 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| dimensional stability | 65.0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60 MPa |
| 3. 20000 hr |
| 4. Without surfactant |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |