| About |
|---|
| Polyamide 6 (PA6) based compound. Heat stabilised. Glass fibres. UL94 V-2 classified, free of halogens-based flame retardants and red phosphorous.&& |
| Product Description | |
|---|---|
| Supplier | LATI |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | V-2,Heat Stabilized,Halogen free,Low to no phosphorus content |
| Availabilitys | Latin America,North America,Africa & Middle East ,Europe,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 0.55 to 0.80 | % | ISO 294-4 |
| MD：2.0 mm | 0.65 to 0.90 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.33 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | ||
| 23℃ | 5500 | MPa | ISO 527-1-2 |
| 60℃ | 4200 | MPa | ISO 527-1-2 |
| 90℃ | 2600 | MPa | ISO 527-1-2 |
| 120℃ | 2100 | MPa | ISO 527-1-2 |
| 150℃ | 1700 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/5 | ||
| Yield, 90 ℃ | 40.0 | MPa | ISO 527-2/5 |
| Yield, 120 ℃ | 35.0 | MPa | ISO 527-2/5 |
| Yield, 150 ℃ | 20.0 | MPa | ISO 527-2/5 |
| tensile strength | ISO 527-2/5 | ||
| Fracture, 23 ℃ | 80.0 | MPa | ISO 527-2/5 |
| Fracture, 60 ℃ | 60.0 | MPa | ISO 527-2/5 |
| Fracture, 90 ℃ | 35.0 | MPa | ISO 527-2/5 |
| Fracture, 120 ℃ | 30.0 | MPa | ISO 527-2/5 |
| Fracture, 150 ℃ | 15.0 | MPa | ISO 527-2/5 |
| Tensile strain | ISO 527-2/5 | ||
| Yield, 90 ℃ | 3.2 | % | ISO 527-2/5 |
| Yield, 120 ℃ | 3.8 | % | ISO 527-2/5 |
| Yield, 150 ℃ | 4.5 | % | ISO 527-2/5 |
| Tensile strain | ISO 527-2/5 | ||
| Fracture, 23 ℃ | 3.5 | % | ISO 527-2/5 |
| Fracture, 60 ℃ | 4.3 | % | ISO 527-2/5 |
| Fracture, 90 ℃ | 7.0 | % | ISO 527-2/5 |
| Fracture, 120 ℃ | 9.0 | % | ISO 527-2/5 |
| Fracture, 150 ℃ | 15 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 30 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 175 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 190 | ℃ | ISO 75-2/B |
| Continuous use temperature | 80.0 | ℃ | |
| Vicat Softening Temp | |||
| B50 | 205 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：30~100℃ | 2.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| Glowing wire flammability index | |||
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 0.75 mm | 775 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 725 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 27 | % | ASTM D2863 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| dimensional stability | 65.0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60 MPa |
| 3. 20000 hr |
| 4. Without surfactant |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |