| About |
|---|
| Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibres.&& |
| Product Description | |
|---|---|
| Supplier | LATI |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Self-lubricating |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 0.90 to 1.2 | % | |
| MD：2.0 mm | 0.40 to 0.60 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 160 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2/5 |
| friction coefficient | ASTM D3702 | ||
| With oneself – dynamic | 0.25 | ||
| With oneself – static | 0.30 | ||
| Wear factor | 1.90E-9 | (m³/h | ASTM D3702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 50 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 100 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 250 | ℃ | ISO 306 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 to 100 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 275 to 300 | °C | |
| Mold temperature | 70.0 to 100 | °C | |
| Injection speed | 中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |