| Leona™ 1300S is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 1300S include automotive, consumer goods, electrical/electronic applications and engineering/industrial parts. Characteristics include: Flame Rated Good Stiffness Good Toughness&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good liquidity |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：2.0 mm | 1.3 | % | ASTM D995 |
| TD：2.0 mm | 2.0 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 2.5 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 230 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 70 | ℃ | ASTM D648 |
| Thermal conductivity coefficient | 0.2 | W/m/K | JIS R2618 |
| Linear coefficient of thermal expansion | |||
| specific heat | 1670 | J/Kg/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Insulation strength | |||
| 20 | KV/mm | ASTM D149 | |
| Dissipation factor | |||
| Compared to the leakage tracing index | 600 | V | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.40mm | V-2 | UL 94 | |
| 0.71mm | V-2 | UL 94 | |
| 1.50mm | V-2 | UL 94 | |
| 3.00mm | V-2 | UL 94 | |
| Extreme oxygen index | 26 | % | ASTM D2863 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 39 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 80 | M 级 | ASTM D785 |
| Rockwell hardness | 120 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 79 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 50 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 118 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2800 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3-6 | Hr | |
| Water content | 0.10 | % | |
| Injection temperature | |||
| Rear barrel temperature | 265-275 | °C | |
| Central temperature of the barrel | 270-280 | °C | |
| Barrel front temperature | 275-285 | °C | |
| Die temperature | 285-295 | °C | |
| Mold temperature | 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |