| Leona™ 14G25是一种聚酰胺66（尼龙66）产品,含有的填充物为25% 玻璃纤维增强材料。 它,在北美洲、非洲和中东、欧洲或亚太地区有供货。 Leona™ 14G25的应用领域包括汽车行业、电气/电子应用 和 工程/工业配件。 特性包括: 阻燃/额定火焰 高刚度 高强度 抗蠕变 耐疲劳&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Fatigue resistance,Heat Resistance, Good,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD | 0.90 | % | Internal Method |
| MD | 0.50 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | — | % | |
| Equilibrium, 23 ℃, 50% RH | — | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 68 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 250 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 245 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 260 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 3.0E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 0.30 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| 23℃ | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 29 | kV/mm | ASTM D149 |
| Dielectric strength | 29 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| 3.00 mm | 425 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 8200 | MPa | ISO 527-2 |
| tensile strength | 180 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 190 | MPa | ISO 527-2 |
| Yield, 23 ℃ | — | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527-2 |
| fracture | 3.0 | % | ASTM D638 |
| Yield, 23 ℃ | — | % | ISO 527-2 |
| Bending modulus | 8100 | MPa | ASTM D790 |
| 23℃ | 7800 | MPa | ISO 178 |
| bending strength | 290 | MPa | ASTM D790 |
| 23℃ | 275 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles | — | mg | ASTM D1044 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 96 | ASTM D785 | |
| R-level | 120 | ASTM D785 | |
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 96 | ISO 2039-2 | |
| R-level | 120 | ISO 2039-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |