| About |
|---|
| UL rated HB. 200 series recommended when V-2 rating required. MFR 10.5. Internal mold release. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HP4.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Food contact compliance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Specific volume | 0.830 | cm³/g | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.15 | % | ASTM D570 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| Equilibrium, 100 ℃ | 0.58 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/2C |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| Colors | 800 | J/m | ASTM D256 |
| Natural，Tints | 800 | J/m | ASTM D256 |
| 23℃ | 800 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 3200 | J/m | ASTM D4812 |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 63.0 | J | ASTM D3763 |
| Drop hammer impact | |||
| 23℃ | 169 | J | ASTM D3029 |
| Tensile impact strength | 577 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 132 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 125 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 6.4 mm | 137 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 136 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | 154 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| A50 | 153 | ℃ | ISO 306/A50 |
| B50 | 141 | ℃ | ISO 306 |
| B120 | 142 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~95℃ | 6.8E-5 | 1/℃ | ASTM E831 |
| specific heat | 1250 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | 0.19 | W/m/K | ASTM C177 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Relative temperature index | |||
| Electrical performance | 130 | ℃ | UL 746 |
| Strength mechanical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in air | 15 | kV/mm | ASTM D149 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 3.17 | ASTM D150 | |
| 60 Hz | 3.17 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 1 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Extreme oxygen index | 25 | % | ASTM D2863 |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 | |
| Transmittance | |||
| 2540 µm | 88.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2370 | MPa | ASTM D638 |
| Tensile modulus | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 68.0 | MPa | ASTM D638 |
| fracture | 70.0 | MPa | ISO 527-2/50 |
| yield | 62.0 | MPa | ASTM D638 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 130 | % | ASTM D638 |
| fracture | 110 | % | ISO 527-2/50 |
| yield | 7.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| Bending modulus | 2300 | MPa | ISO 178 |
| 50 mm span | 2340 | MPa | ASTM D790 |
| bending strength | 90.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 97.0 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 10.0 | mg | ASTM D1044 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 70 | ASTM D785 | |
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Suggested injection volume | 40 to 60 | % | |
| Temperature at the rear of the barrel | 271 to 293 | °C | |
| Temperature in the middle of the barrel | 282 to 304 | °C | |
| Front temperature of material barrel | 293 to 316 | °C | |
| Nozzle temperature | 288 to 310 | °C | |
| Processing (melt) temperature | 293 to 316 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Exhaust hole depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 |
| 8. Type S |
| 9. 120*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |