| SABIC的LEXAN™树脂151是无定形聚碳酸酯（PC）级。具有出色的机械，光学，电气和热性能。提供抗冲击性，出色的尺寸稳定性和晶体透明度。LEXAN™树脂151适用于注塑和吹塑加工。符合UL 94 HB防火等级。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,Good Dimensional Stability |
| Availabilitys | Africa & Middle East ,North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Yield, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, Type I, 50 mm/min | 66 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 50 mm/min | 7 | % | ASTM D638 |
| Tensile strain | |||
| Fracture, 50 mm/min | 110 | % | ASTM D638 |
| bending strength | |||
| Yield, 1.30 mm/min, 0 mm span | 92.214 | MPa | ASTM D790 |
| Bending modulus | |||
| 2344.59 | MPa | ASTM D790 | |
| Rockwell hardness | |||
| M-level | 70 | ASTM D785 | |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| Taber wear and tear | |||
| CS-17，1kg | 10 | mg/1000cy | ASTM D1044 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 3194.8 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 744.8 | J/m | ASTM D256 |
| Tensile impact | |||
| S-shaped | 642 | cm-kgf/cm² | ASTM D 1822 |
| Drop hammer impact | |||
| D 3029，23℃ | 170 | n.m | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 157 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 137 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 6.84E-05 | 1/℃ | ASTM E831 |
| specific heat | 1.25 | J/g-℃ | ASTM C 351 |
| Thermal conductivity coefficient | 0.19 | W/m/℃ | ASTM C 177 |
| Relative temperature index | |||
| Non mechanical impact performance | 125 | ℃ | UL 746B |
| Electrical performance | 125 | ℃ | UL 746B |
| Impact mechanical performance | 115 | ℃ | UL 746B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.2 | ASTM D792 | |
| Specific volume | 0.83 | cm³/g | ASTM D 792 |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| Water absorption rate | |||
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| Equilibrium, 100 ℃ | 0.58 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：24 hrs | 0.5-0.7 | % | Internal Method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 2.5 | g/10min | ASTM D1238 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 88 | % | ASTM D1003 |
| Haze | 1 | % | ASTM D1003 |
| Refractive index | 1.586 | ASTM D542 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | >1.E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in air | 14.9 | kV/mm | ASTM D149 |
| Relative permittivity | |||
| 50-60 Hz | 3.17 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| Dissipation factor | |||
| 50-60 Hz | 0.0009 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.01 | ASTM D150 | |
| Arc resistance | |||
| Tungsten wire | 5 | PLC Code | ASTM D495 |
| Hot wire ignition {PLC} | 4 | PLC Code | UL 746A |
| High voltage arc marking rate {PLC} | 2 | PLC Code | UL 746A |
| High current arc ignition (surface {PLC}) | 2 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 2 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 94HB flame rating assessment | 1.47 | mm | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion blow molding | Nominal value | Unit | Test method |
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2 – 4 | hrs | |
| Maximum water content | 0.02 | % | |
| Minimum moisture content | 0.01 | % | |
| Mold temperature (billet) | 265 – 280 | °C | |
| Temperature of barrel heating zone 1 | 260 – 290 | °C | |
| Temperature of barrel heating zone 2 | 260 – 290 | °C | |
| Temperature of barrel heating zone 3 | 260 – 290 | °C | |
| Temperature of barrel heating zone 4 | 260 – 290 | °C | |
| Adjust the temperature in Zone 5 | 260 – 290 | °C | |
| Mold temperature | 60 – 100 | °C | |
| Drying temperature | 120 | °C | |
| Drying time | 3 – 4 | hrs | |
| Drying time (gradually increasing) | 48 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 320 – 345 | °C | |
| Nozzle temperature | 315 – 340 | °C | |
| Front temperature | 320 – 345 | °C | |
| Mid section temperature | 310 – 330 | °C | |
| Post stage temperature | 300 – 320 | °C | |
| Mold temperature | 80 – 115 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 40 – 70 | rpm | |
| Shooting cylinder size | 40 – 60 | % | |
| Depth of exhaust groove | 0.025 – 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |