| LEXAN 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in various opaque color options. LEXAN 3412ECR is a resin designed to meet the needs of high stiffness applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Halogen free,Flame Characteristics,V-0,5VA |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 7.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 7.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.20 to 0.50 | % | Internal Method |
| MD：3.2 mm | 0.20 to 0.50 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.29 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.12 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5500 | MPa | ASTM D638 |
| Tensile modulus | 6000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 87.0 | MPa | ASTM D638 |
| fracture | 90.0 | MPa | ISO 527-2/5 |
| yield | 95.0 | MPa | ISO 527-2/5 |
| yield | 90.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.2 | % | ISO 527-2/5 |
| yield | 2.8 | % | ISO 527-2/5 |
| yield | 3.1 | % | ASTM D638 |
| Bending modulus | 5500 | MPa | ISO 178 |
| 50 mm span | 5000 | MPa | ASTM D790 |
| bending strength | 140 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 156 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 40 | kJ/m² | ISO 179/1eU |
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 110 | J/m | ASTM D256 |
| 23℃ | 110 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 35 | kJ/m² | ISO 180/1U |
| 23℃ | 35 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 20.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 136 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 141 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 141 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | 147 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 145 | ℃ | ISO 306 |
| B120 | 146 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 3.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 3.0E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 130 | ℃ | UL 746 |
| Strength mechanical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.30 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 0.020 | IEC 60250 | |
| 60 Hz | 0.020 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 3 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 825 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 40 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 266 to 288 | °C | |
| Barrel middle temperature | 277 to 299 | °C | |
| Barrel front temperature | 288 to 310 | °C | |
| Nozzle temperature | 282 to 304 | °C | |
| Processing (melt) temperature | 288 to 310 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 11. Tungsten Electrode |
| 12. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |