| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | V-1,Flame Characteristics,Good Rigidity |
| Availabilitys | Europe,North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| proportion | 1.35 | ASTM D792 | |
| Melt Volume Rate | |||
| 300℃，1.2 kgf | 4.3 | g/10min | ASTM D1238 |
| Mold shrinkage rate | |||
| 3.2 mm, flowing | 0.10 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hrs | 0.16 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.29 | % | ASTM D570 |
| Specific volume | 0.74 | cm³/g | ASTM D792 |
| Density | 1.356 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress | |||
| Fracture, Type I, 5mm/min | 110 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 5mm/min | 5 | % | ASTM D638 |
| Bending modulus | |||
| 1.3mm/min, 50mm span | 5510 | MPa | ASTM D790 |
| Bending stress | |||
| Yield, 1.3mm/min, 50mm span | 131 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 91 | ASTM D-785 | |
| Rockwell hardness | |||
| R-level | 122 | ASTM D-785 | |
| Taber abraser | |||
| CS17,1kg | 17 | mg/1000cy | ASTM D1044 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 1014 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 106 | J/m | ASTM D256 |
| Tensile impact strength | |||
| S-shaped | 63 | KJ/m² | ASTM D1822 |
| Drop hammer impact | |||
| 23℃ | 5 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.82 MPa, unannealed, 6.4 mm | 146 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 148 | ℃ | ASTM D648 |
| Vicat Softening Temp | 165 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| -40~95 ℃, flowing | 2.7E-5 | 1/℃ | ASTM E831 |
| specific heat | 1.17 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | 0.21 | W/m/K | ASTM C177 |
| Relative temperature index | |||
| Electrical performance | 130 | ℃ | UL-746B |
| Mechanical impact performance | 130 | ℃ | UL-746B |
| Non mechanical impact performance | 130 | ℃ | UL-746B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+17 | Ω·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in air | 19.2 | kV/mm | ASTM D149 |
| Relative dielectric constant | ASTM D150 | ||
| 50 Hz | 3.17 | ASTM D150 | |
| 60 Hz | 3.17 | ASTM D150 | |
| 1MHz | 3.13 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 7.3E-3 | ASTM D150 | |
| Arc resistance | PLC 7 | PLC Code | ASTM D495 |
| Compared to the leakage tracing index | PLC 5 | PLC Code | UL 746A |
| High Arc Burning Index (HAI) | PLC 4 | PLC Code | UL 746A |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | PLC Code | UL 746A |
| Hot wire ignition | |||
| HWI | PLC 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| UL flame retardant rating | |||
| 94V-1 | 1.47 | mm | UL 94 |
| 94V-0 | 2.99 | mm | UL 94 |
| 94-5VA | 2.99 | mm | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hrs | |
| Drying time, cumulative | 48 | hrs | |
| Recommended maximum moisture content | 0.020 | % | |
| Suggested injection volume | 40 to 60 | % | |
| Temperature at the rear of the barrel | 295 to 315 | °C | |
| Temperature in the middle of the barrel | 305 to 325 | °C | |
| Front temperature of material barrel | 315 to 340 | °C | |
| Nozzle temperature | 310 to 330 | °C | |
| Processing (melt) temperature | 315 to 340 | °C | |
| Mold temperature | 80 to 115 | °C | |
| Back pressure | 0.3 to 0.7 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Exhaust hole depth | 0.025 to 0.076 | mm | |
| Shoot to cylinder size | 40 to 60 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |