| About |
|---|
| LEXAN™ 3414R resin 40% GR, provides improved mechanical properties and UL94V-1 rated at 0.058″. Internal mold release added.&&LEXAN™ 3414R resin LEXAN 3414R is a high viscosity, 40% glass reinforced, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Viscosity,Flame Characteristics,High Heat Resistance,V-1,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific volume | 0.658 | cm³/g | ASTM D792 |
| Density | 1.52 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 13 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.10 to 0.20 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃ | 0.23 | % | ASTM D570 |
| 24hr | 0.12 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 1300 | J/m | ASTM D4812 |
| 23℃ | 130 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 23℃ | 6.78 | J | ASTM D3029 |
| Tensile impact strength | 67.2 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 146 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 154 | ℃ | ASTM D648 |
| Vicat Softening Temp | 166 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 1.6E-5 | 1/℃ | ASTM E831 |
| specific heat | 1050 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | 0.22 | W/m/K | ASTM C177 |
| Relative temperature index | |||
| Electrical performance | 130 | ℃ | UL 746 |
| Strength mechanical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in air | 18 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 3.53 | ASTM D150 | |
| 60 Hz | 3.53 | ASTM D150 | |
| 1 MHz | 3.48 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 1.3E-3 | ASTM D150 | |
| 60 Hz | 1.3E-3 | ASTM D150 | |
| 1 MHz | 6.7E-3 | ASTM D150 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 4 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.10 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 125 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 9650 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 186 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 32.0 | mg | ASTM D1044 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 93 | ASTM D785 | |
| R-level | 119 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 293 to 316 | °C | |
| Barrel middle temperature | 304 to 327 | °C | |
| Barrel front temperature | 316 to 338 | °C | |
| Nozzle temperature | 310 to 332 | °C | |
| Processing (melt) temperature | 316 to 338 | °C | |
| Mold temperature | 82 to 116 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |