| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Fracture, Type I, 50 mm/min | 68 | MPa | ASTM D638 |
| Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 125 | % | ASTM D638 |
| Type I, 50 mm/min | 6 | % | ASTM D638 |
| Tensile modulus | |||
| 50 mm/min | 2266.11 | MPa | ASTM D638 |
| bending strength | |||
| Yield, 1.30 mm/min, 50 mm span | 100.062 | MPa | ASTM D790 |
| Bending modulus | |||
| 2364.21 | MPa | ASTM D790 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 793.8 | J/m | ASTM D256 |
| Total energy of instrument impact | |||
| 23℃ | 805 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 143 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 126 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 137 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.38E-05 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 6.84E-05 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Non mechanical impact performance | 130 | ℃ | UL 746B |
| Electrical performance | 130 | ℃ | UL 746B |
| Impact mechanical performance | 120 | ℃ | UL 746B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.19 | ASTM D792 | |
| Shrinkage rate | |||
| MD：3.2 mm | 0.6 – 0.8 | % | Internal Method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 7 | g/10min | ASTM D1238 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | |||
| Tungsten wire | 7 | PLC | ASTM D495 |
| Hot wire ignition {PLC} | 3 | PLC | UL 746A |
| High voltage arc marking rate {PLC} | 3 | PLC | UL 746A |
| High current arc ignition (surface {PLC}) | 2 | PLC | UL 746A |
| Compared to the leakage tracing index | 3 | PLC | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.52 mm | V-2 | UL 94 | |
| 3.04 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 960 ℃, passed through | 1 | mm | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 875 | ℃ | IEC 60695-2-13 |
| ultraviolet radiation | |||
| Water exposure/soaking | F1 | UL 746C |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | ＞85 | % | ASTM D1003 |
| Haze | 1 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 120 | °C | |
| Drying time | 2 – 4 | hrs | |
| Maximum moisture content | 0.02 | % | |
| Melt Temperature | 290 – 320 | °C | |
| Melt Temperature | 280 – 310 | °C | |
| Front Section Zone 3 Temperature | 290 – 320 | °C | |
| Temperature in Zone 2 of the middle section | 280 – 310 | °C | |
| Temperature in Zone 1 of the rear section | 270 – 300 | °C | |
| Hopper temperature | 60 – 80 | °C | |
| Mold temperature | 80 – 120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |