Lexan™ BFL2000U Resin

About
Lexan * BFL2000U聚碳酸酯（PC）树脂是注塑成型品。它含有UL-94 V0rating的非溴化，非氯化阻燃体系。 Lexan * BFL2000U专为具有耐候性的高反射率应用而设计。

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	Weather resistance is good,Halogen free
Availabilitys	Africa & Middle East ,North America,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile strength yield type I 50mm/min	610	kgf/cm²	ASTM D 638
Tensile strength fracture type I 50 mm/min	500	kgf/cm²	ASTM D 638
Tensile strain
Yield, Type I, 50 mm/min	5	%	ASTM D638
Tensile strain
Fracture, Type I, 50 mm/min	80	%	ASTM D638
bending strength
Yield, 50 mm span	92.214	MPa	ASTM D790
Bending modulus
	2246.49	MPa	ASTM D638
Tensile strength
Fracture 50mm/min	52	MPa	ISO 527
Yield 50 millimeters/minute	60	MPa	ISO 527
Stretch elongation
Fracture 50mm/min	70	%	ISO 527
Yield 50 millimeters/minute	5	%	ISO 527
Tensile modulus
50 mm/min	2197.44	MPa	ASTM D638
1 mm/min	2650	MPa	ISO 527
bending strength
Yield, 2 mm/min	90	MPa	ISO 178
Bending modulus
2 mm/mim	2300	MPa	ISO 527

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	617.4	J/m	ASTM D256
Impact strength of cantilever beam notch
-30℃	196	J/m	ASTM D256
Instrument control anti impact total energy 23 ℃	560	cm-kgf	ASTM D 3763
Notched impact strength of cantilever beam
23℃，80103	NB	kJ/m²	ISO 180/1U
Notched impact strength of cantilever beam
-30℃，80103	NB	kJ/m²	ISO 180/1U
Impact strength of cantilever beam notch
23℃，80103	11	kJ/m²	ISO 180-1U
Impact strength of cantilever beam notch
-30℃，80103	10	kJ/m²	ISO 180-1U
Charpy Notched Impact Strength
23℃	NB	kJ/m²	ISO 179/1eU
23℃	12	kJ/m²	ISO 179/1eU
-30℃	NB	kJ/m²	ISO 179/1eU
-30℃	11	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	138	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, unannealed, 3.2 mm	120	℃	ASTM D648
1.8 MPa, unannealed, 64 mm span	120	℃	ISO 75/BF
0.45 MPa, unannealed, 64 mm span	132	℃	ISO 75/BF
0.45 MPa, unannealed, 3.2 mm	132	℃	ASTM D648
Linear coefficient of thermal expansion
TD：-23~40℃	7.E-05	1/℃	ISO 11359-2
MD：-30~40℃	7.E-05	1/℃	ASTM D696
MD：-23~40℃	7.E-05	1/℃	ISO 11359-2
MD：-23~40℃	7.E-05	1/℃	ASTM D648
Ball pressure test
125℃±2℃	PASS		IEC 60695-10-2
Vicat Softening Temp	139	℃	ISO 306
Vicat Softening Temp	141	℃	ISO 306
Relative heat index	80	℃	UL 746B
Non mechanical impact performance	80	℃	UL 746B
Mechanical impact	80	℃	UL 746B

PHYSICAL	Nominal value	Unit	Test method
Density	1.29	g/cm³	ISO 1183
Water absorption rate
24hr	0.35	%	ISO 62
Shrinkage rate
MD：3.2 mm	0.15	%	ISO 62
Melt Flow Rate
300℃，5.0kg	24	g/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index	2	PLC Code	UL 746A
Compared to the leakage tracing index	350	v	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94V-0	1.5	mm	UL 94
Flame retardant grade 94V-2	0.75	mm	UL 94

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.