| About |
|---|
| LEXAN 943X is a UV stabilized medium flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN 943X resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,High impact resistance,Ductility,Quick molding cycle,Halogen free,Flame Characteristics,Moderate liquidity |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.18 | g/cm³ | ASTM D792 |
| — | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.80 | % | |
| TD：3.2 mm | 0.40 to 0.80 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2100 | MPa | ASTM D638 |
| — | 2100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 60.0 | MPa | ASTM D638 |
| fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 130 | % | ASTM D638 |
| fracture | 130 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2060 | MPa | ASTM D790 |
| — | 2200 | MPa | ISO 178 |
| bending strength | |||
| — | 85.0 | MPa | ISO 178 |
| Yield, 50 mm span | 89.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 60 | kJ/m² | |
| 23℃ | 75 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 650 | J/m | ASTM D256 |
| 23℃ | 800 | J/m | ASTM D256 |
| -30℃ | 50 | kJ/m² | ISO 180-1A |
| 23℃ | 70 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 50.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 135 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 120 | ℃ | |
| Vicat Softening Temp | |||
| B120 | 140 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 123~127℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 6.5E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 6.5E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 7.7E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 120 | ℃ | UL 746 |
| Electrical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | ASTM D149 |
| 3.2 mm in oil | 16 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 60 Hz | 2.95 | ||
| 50 kHz | 2.95 | ||
| 1 MHz | 2.90 | ||
| Dissipation factor | |||
| 50 Hz | 2.4E-3 | ||
| 60 Hz | 2.4E-3 | ||
| 1 MHz | 8.5E-3 | ||
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 1 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 825 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 215 to 295 | °C | |
| Barrel middle temperature | 280 to 305 | °C | |
| Barrel front temperature | 295 to 315 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Processing (melt) temperature | 295 to 315 | °C | |
| Mold temperature | 70 to 95 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 10. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |