| About |
|---|
| LEXAN EXL1162T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. LEXAN EXL1162T resin is a general purpose product available in transparent and opaque colors and may be an excellent candidate for a broad range of applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High liquidity,Ductility,Quick molding cycle,Good stripping performance,Copolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 20 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 19.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.80 | % | |
| TD：3.2 mm | 0.40 to 0.80 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.12 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.090 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 45 | kJ/m² | |
| 23℃ | 65 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| Impact strength of cantilever beam notch | |||
| -30℃ | 620 | J/m | ASTM D256 |
| 23℃ | 740 | J/m | ASTM D256 |
| -30℃ | 40 | kJ/m² | ISO 180-1A |
| 23℃ | 55 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 74.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 121 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 116 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 138 | ℃ | ASTM D1525 11 |
| B120 | 139 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 123~127℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 7.5E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~95℃ | 7.6E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 7.6E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 130 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 0.8 mm | 850 | ℃ | |
| 3 mm | 850 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2540 µm | 82.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | 3.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| Level L | 89 | ISO 2039-2 | |
| Tensile modulus | |||
| — | 2260 | MPa | ASTM D638 |
| — | 2340 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 57.0 | MPa | ISO 527-2/50 |
| fracture | 57.0 | MPa | ASTM D638 |
| fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.7 | % | ASTM D638 |
| yield | 5.4 | % | ISO 527-2/50 |
| fracture | 120 | % | ASTM D638 |
| fracture | 120 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2240 | MPa | ASTM D790 |
| — | 2140 | MPa | ISO 178 |
| bending strength | |||
| — | 89.0 | MPa | ISO 178 |
| Yield, 50 mm span | 94.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 215 to 295 | °C | |
| Barrel middle temperature | 280 to 305 | °C | |
| Barrel front temperature | 295 to 315 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Processing (melt) temperature | 295 to 315 | °C | |
| Mold temperature | 70 to 95 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |