| About |
|---|
| XHT3146 is a high mold release version of XHT3141 high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good stripping performance,High Heat Resistance,Copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 16.0 | cm³/10min | |
| 330℃，2.16 kg | 30.0 | cm³/10min | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.30 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2700 | MPa | ASTM D638 |
| — | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 70.0 | MPa | ASTM D638 |
| yield | 70.0 | MPa | ISO 527-2/50 |
| fracture | 55.0 | MPa | ASTM D638 |
| fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 70 | % | ASTM D638 |
| fracture | 70 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2600 | MPa | ASTM D790 |
| — | 2500 | MPa | ISO 178 |
| bending strength | |||
| — | 80.0 | MPa | ISO 178 |
| Yield, 50 mm span | 120 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 11 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 55 | J/m | ASTM D256 |
| 23℃ | 97 | J/m | ASTM D256 |
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 9.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 68.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 166 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 4.0 mm, 64 mm span | 164 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 156 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 152 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 170 | ℃ | ASTM D1525 10 |
| B50 | 168 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 6.0E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 6.0E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 6.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | |||
| 25℃ | 0.20 | W/m/K | ASTM C177 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 270 to 330 | °C | |
| Barrel middle temperature | 280 to 340 | °C | |
| Barrel front temperature | 290 to 350 | °C | |
| Nozzle temperature | 285 to 345 | °C | |
| Processing (melt) temperature | 290 to 350 | °C | |
| Mold temperature | 95 to 130 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 90 | rpm | |
| Vent depth | 0.025 to 0.080 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |