LEXAN™ DMX1132 resin

About
LEXAN™ DMX1132是一种高流动性的聚碳酸酯共聚物树脂，与普通聚碳酸酯树脂的耐氨性相对较强。

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	High liquidity,Ammonium-tolerant
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 50 mm/min	73	MPa	ISO 527
Fracture, 50 mm/min	55	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	7	%	ISO 527
Fracture, 50 mm/min	>25	%	ISO 527
Tensile modulus
1 mm/min	2400	MPa	ISO 527
bending strength
Yield, 2 mm/min	100	MPa	ISO 527
Bending modulus
2 mm/mim	2500	MPa	ISO 527
Ball hardness
H358/30	110	MPa	ISO 2039-1
pencil hardness test
1kgf	HB		ASTM D 3363
Erikson scratch depth
6N	17	micromete	SABIC Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	9.8	J/m	ASTM D256
23℃，80103	5	kJ/m²	ISO 180-1A
-30℃，80103	3	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80 * 10 * 3, 62mm span
80 * 10 * 3, 62mm span
23℃	3	kJ/m²	ISO 179/1eA
-30℃	5	kJ/m²	ISO 179/1eA
23℃	NB	kJ/m²	ISO 179/1eU
-30℃	90	kJ/m²	ISO 179/1eU
Notched impact strength of cantilever beam
23℃，80103	NB	kJ/m²	ISO 180/1U
-30℃，80103	NB	kJ/m²	ISO 180/1U
Total energy of instrument impact
23℃	734	cm-kgf	ASTM D 3763

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	137	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, unannealed, 64 mm span	133	℃	ISO 75/Bf
1.8 MPa, unannealed, 64 mm span	120	℃	ISO 75/Af
Unannealed, 3.2 mm
0.45 MPa	132	℃	ASTM D 648
1.8MPa	121	℃	ASTM D 648
Linear coefficient of thermal expansion
MD：-40~95℃	7.E-05	1/℃	ASTM E831
TD：-40~95℃	7.E-05	1/℃	ASTM E831
Thermal conductivity coefficient
	0.2	W/m/℃	ASTM C177
	0.2	W/m/℃	ISO 8302
Linear coefficient of thermal expansion
MD：23~80℃	7.E-05	1/℃	ISO 11359-2
TD：23~80℃	7.E-05	1/℃	ISO 11359-2
Vicat Softening Temp
B50	140	℃	ISO 306
B120	141	℃	ISO 306

PHYSICAL	Nominal value	Unit	Test method
Density	1.2		ASTM D792
Shrinkage rate
MD：3.2 mm	0.6 – 0.8	%	Internal Method
TD：3.2 mm	0.6 – 0.8	%	Internal Method
Melt Flow Rate
300℃，1.20kg	38.5	g/10min	ASTM D1238
Density	1.19	g/cm³	ISO 1183
Melt Volume Rate
300℃，1.2 kg	36	cm³/10min	ISO 1133

optical performance	Nominal value	Test method
Refractive index
	1.586	ASTM D542
	1.586	ISO 489

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	3 – 4	hrs
Drying time (cumulative)	0.02	%
Melt temperature	295 – 315	°C
Nozzle temperature	290 – 310	°C
Front Section Zone 3 Temperature	295 – 315	°C
Temperature in Zone 2 of the middle section	280 – 305	°C
Temperature in Zone 1 of the rear section	260 – 280	°C
Hopper temperature	60 – 80	°C
Mold temperature	70 – 95	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.