| About |
|---|
| 汽车内饰 10％玻璃增强。增加刚度/结构刚度。高模量，流延性。发泡表面仪表板也可使用 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High modulus,Flow ductility |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Fracture, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 14 | % | ASTM D638 |
| bending strength | |||
| Yield, 50 mm span | 93.195 | MPa | ASTM D790 |
| Bending modulus | |||
| 1.3 mm/min，50mm跨距 | 2756.61 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 205.8 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 127.4 | J/m | ASTM D256 |
| -30℃ | 156.8 | J/m | ASTM D256 |
| Instrument impact energy peak | |||
| 23℃ | 253 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 137 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 3.6E-05 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Non mechanical impact performance | 80 | ℃ | UL 746B |
| Electrical performance | 80 | ℃ | UL 746B |
| Impact mechanical performance | 80 | ℃ | UL 746B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.24 | ASTM D792 | |
| Water absorption rate | |||
| 24hr | 0.14 | % | ASTM D570 |
| Shrinkage rate | 0.3 – 0.5 | % | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 94HB flame level | 1.49 | mm | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3 – 4 | hrs | |
| Drying time (cumulative) | 48 | hrs | |
| Maximum moisture content | 0.02 | % | |
| Melt temperature | 295 – 315 | °C | |
| Nozzle temperature | 290 – 310 | °C | |
| Front Section Zone 3 Temperature | 295 – 315 | °C | |
| Temperature in Zone 2 of the middle section | 280 – 305 | °C | |
| Temperature in Zone 1 of the rear section | 270 – 295 | °C | |
| Mold temperature | 70 – 95 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 40 – 70 | rpm | |
| Shoot to cylinder size | 40 – 60 | % | |
| Depth of exhaust groove | 0.025 – 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |