| About |
|---|
| LEXAN™ EXL AMHI240F filament is a high impact polycarbonate product available in a black color. It provides high impact strength at room temperature and extreme low temperatures, in combination with improved UL94 performance over standard polycarbonate. Nominal filament diameter is 1.79 mm ± 0.05 mm and it is available in a 1510 cc spool size.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| XY direction | 1700 | MPa | |
| XZ direction | 1900 | MPa | |
| ZX direction | 1790 | MPa | |
| tensile strength | |||
| XY direction, fracture | 45.0 | MPa | |
| XZ direction, fracture | 55.0 | MPa | |
| ZX direction, fracture | 40.0 | MPa | |
| Tensile strain | |||
| XY direction, fracture | 7.0 | % | |
| XZ direction, fracture | 5.0 | % | |
| ZX direction, fracture | 3.0 | % | |
| Bending modulus | |||
| XY direction | 1510 | MPa | |
| XZ direction | 1900 | MPa | |
| ZX direction | 1470 | MPa | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| XY direction, -30 ℃ | 190 | J/m | |
| XY direction, 23 ℃ | 210 | J/m | |
| XZ direction, -30 ℃ | 260 | J/m | |
| XZ direction, 23 ℃ | 310 | J/m | |
| ZX direction, -30 ℃ | 40 | J/m | |
| ZX direction, 23 ℃ | 55 | J/m | |
| Notched impact strength of cantilever beam | |||
| ZX direction: -30 ℃ | 300 | J/m | |
| XZ direction: -30 ℃ | 860 | J/m | |
| XY direction: -30 ℃ | 980 | J/m | |
| ZX direction: 23 ℃ | 260 | J/m | |
| XZ direction: 23 ℃ | 810 | J/m | |
| XY direction: 23 ℃ | 850 | J/m | |
| Dart impact equipped with measuring instruments | |||
| -30℃，Total Energy | 11.0 | J | |
| -30℃，Total Energy | 13.0 | J | |
| 23℃，Total Energy | 14.0 | J | |
| 23℃，Total Energy | 16.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| XY direction: 1.8 MPa, unannealed, 3.20 mm | 140 | ℃ | |
| XZ direction: 1.8 MPa, unannealed, 3.20 mm | 139 | ℃ | |
| ZX direction: 1.8 MPa, unannealed, 3.20 mm | 138 | ℃ | |
| Vicat Softening Temp | |||
| — | 148 | ℃ | ASTM D1525 6 |
| — | 149 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | |||
| MD: XY direction | 7.7E-5 | 1/℃ | |
| MD: ZX direction | 7.9E-5 | 1/℃ | |
| MD: XZ direction | 8.0E-5 | 1/℃ | |
| TD: XY direction | 7.7E-5 | 1/℃ | |
| TD: ZX direction | 7.9E-5 | 1/℃ | |
| TD: XZ direction | 8.1E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| XY direction | 3.2E+14 | ohms·cm | |
| ZX direction | 2.4E+14 | ohms·cm | |
| Dissipation factor | |||
| XY direction: 1.90 GHz | 5.0E-3 | ||
| ZX direction: 1.90 GHz | 5.0E-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| ZX direction, 3.00 mm | V-2 | ||
| XZ direction, 3.00 mm | V-0 | ||
| XY direction, 3.00 mm | V-0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. 0.051 in/min |
| 4. XY Orientation |
| 5. ZX Orientation |
| 6. Rate A (50°C/h), Loading 1 (10 N) |
| 7. UL results provided herein may not be sufficient to waive end use part testing for UL listing. Contact UL for further details. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |