| LEXAN EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1330 resin is a general purpose product available in a wide range of opaque colors and is an excellent candidate for a broad range of applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.40 to 0.80 | % | Internal Method |
| MD：3.2 mm | 0.40 to 0.80 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 60 | kJ/m² | ISO 179/1eA |
| 23℃ | 75 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -50℃ | 590 | J/m | ASTM D256 |
| -30℃ | 680 | J/m | ASTM D256 |
| 23℃ | 800 | J/m | ASTM D256 |
| 23℃，6.4mm | 640 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 55 | kJ/m² | ISO 180-1A |
| 23℃ | 70 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 1100 | J/m | Internal Method |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | No Break | ISO 180/1U | |
| 23℃ | No Break | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 52.9 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 100 mm span | 125 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 3.2 mm | 134 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 136 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 121 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 124 | ℃ | ASTM D648 |
| Vicat Softening Temp | 143 | ℃ | ASTM D1525 11 |
| Vicat Softening Temp | |||
| B50 | 143 | ℃ | ISO 306 |
| B120 | 145 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：23~80℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 125 | ℃ | UL 746 |
| Strength mechanical performance | 120 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.80 mm | 850 | ℃ | IEC 60695-2-12 |
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 875 | ℃ | IEC 60695-2-13 |
| 3 mm | 875 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 35 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2100 | MPa | ASTM D638 |
| Tensile modulus | 2100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 61.4 | MPa | ASTM D638 |
| fracture | 56.0 | MPa | ISO 527-2/50 |
| yield | 58.6 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 130 | % | ASTM D638 |
| fracture | > 100 | % | ISO 527-2/50 |
| yield | 6.0 | % | ASTM D638 |
| yield | 5.0 | % | ISO 527-2/50 |
| Bending modulus | 2100 | MPa | ISO 178 |
| 50 mm span | 2070 | MPa | ASTM D790 |
| bending strength | 85.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 88.9 | MPa | ASTM D790 |
| Ball hardness | |||
| H358/30 | 90.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 217 to 293 | °C | |
| Barrel middle temperature | 282 to 304 | °C | |
| Barrel front temperature | 293 to 316 | °C | |
| Nozzle temperature | 288 to 310 | °C | |
| Processing (melt) temperature | 293 to 316 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Drying temperature | 110 to 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 249 to 288 | °C | |
| Barrel 2 zone temperature | 243 to 271 | °C | |
| Barrel 3 zone temperature | 227 to 254 | °C | |
| Connector temperature | 227 to 254 | °C | |
| Melt temperature | 243 to 260 | °C | |
| Nozzle temperature | 238 to 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. Double-gated |
| 9. 80*10*3 mm |
| 10. 120*10*4 mm |
| 11. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |