| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,High Viscosity,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 50% RH， 23℃ | 0.15 | % | ISO 62 |
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 50 mm/min | ＞60 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, 50 mm/min | 6.0 | % | ISO 527 |
| Fracture, 50 mm/min | 100 | % | ISO 527 |
| Tensile modulus | |||
| 1 mm/min | 2300 | MPa | ISO 527 |
| bending strength | |||
| Yield, 2 mm/min | 90 | MPa | ISO 178 |
| Bending modulus | |||
| Yield, 2 mm/min | 2300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.0mm | 80 | kJ/m² | ISO 180/1U |
| Notched impact strength of cantilever beam | |||
| 23℃，3.0mm | 无断裂 | ISO 180/1U | |
| Charpy Notched Impact Strength | |||
| 3.0mm | 75 | kJ/m² | ISO 179/1C |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 127 | ℃ | ISO 75 |
| Vicat Softening Temp | 145 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD： 23-55°C | 7×10-5 | 1/℃ | ISO 75 |
| Ball pressure color measurement | IEC 60695-10-2 | ||
| 125±2S℃ | 通过 | ||
| Thermal conductivity coefficient | 0.2 | W/m.°C | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ＞1E+15 | Ohm.cm | IEC 60093 |
| Dielectric strength | |||
| In oil, 3.2mm | 18 | kV/mm | IEC 60243-1 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |