| About |
|---|
| LEXAN HFD4472 is a 20% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4472 has enhanced mold release, impact ductility and broad color space.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Ductility,Good stripping performance,Moderate liquidity,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.40 to 0.50 | % | Internal Method |
| MD：3.2 mm | 0.20 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.12 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5500 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 56.0 | MPa | ASTM D638 |
| fracture | 56.0 | MPa | ISO 527-2/5 |
| yield | 54.0 | MPa | ASTM D638 |
| yield | 54.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/5 |
| yield | 2.0 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 4900 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 93.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 13 | kJ/m² | ISO 179/1eA |
| 23℃ | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 59 | kJ/m² | ISO 179/1eU |
| 23℃ | 59 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 800 | J/m | ASTM D4812 |
| 23℃ | 190 | J/m | ASTM D256 |
| -30℃ | 13 | kJ/m² | ISO 180-1A |
| 23℃ | 18 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 43 | kJ/m² | ISO 180/1U |
| 23℃ | 47 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 30.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 128 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B120 | 135 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：23~80℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 8.0E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 3.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 3.0E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 80.0 | ℃ | UL 746 |
| Strength mechanical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.9 GHz | 3.16 | Internal Method | |
| Dissipation factor | |||
| 1.9 GHz | 9.9E-3 | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 266 to 288 | °C | |
| Barrel middle temperature | 277 to 299 | °C | |
| Barrel front temperature | 288 to 310 | °C | |
| Nozzle temperature | 282 to 304 | °C | |
| Processing (melt) temperature | 288 to 310 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 80*10*3 sp=62mm |
| 6. 80*10*3 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |