| About |
|---|
| LEXAN 945U Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has a UL-94 V0 rating and is UV stabilized, providing additional weathering capability. LEXAN 945U resin is available in various opaque color options and is a general-purpose resin ideal for a wide variety of applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.80 | % | Internal Method |
| Outdoor applicability | f1 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2270 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 62.0 | MPa | |
| fracture | 65.0 | MPa | |
| Tensile strain | |||
| yield | 6.0 | % | |
| fracture | 130 | % | |
| Bending modulus | |||
| 50 mm span | 2340 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 101 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 800 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 73.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 137 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 126 | ℃ | |
| Vicat Softening Temp | 143 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 6.7E-5 | 1/℃ | |
| TD：-40~40℃ | 6.7E-5 | 1/℃ | |
| Relative temperature index | 130 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 120 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 2 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1.5 mm | 800 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 270 to 295 | °C | |
| Barrel middle temperature | 280 to 305 | °C | |
| Barrel front temperature | 295 to 315 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Processing (melt) temperature | 295 to 315 | °C | |
| Mold temperature | 70 to 95 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 6. Tungsten Electrode |
| 7. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |