| Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.23 | g/cm³ | ASTM D792 |
| — | 1.30 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 6.5 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | |
| MD：3.2 mm | 0.20 to 0.50 | % | |
| TD：3.2 mm | 0.20 to 0.50 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 5330 | MPa | ASTM D638 |
| — | 4950 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 92.0 | MPa | ASTM D638 |
| yield | 103 | MPa | ISO 527-2/50 |
| fracture | 91.0 | MPa | ASTM D638 |
| fracture | 100 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.5 | % | ASTM D638 |
| yield | 3.6 | % | ISO 527-2/50 |
| fracture | 4.0 | % | ASTM D638 |
| fracture | 4.3 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 4600 | MPa | ASTM D790 |
| — | 4280 | MPa | ISO 178 |
| bending strength | |||
| — | 150 | MPa | ISO 178 |
| Yield, 50 mm span | 156 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| -30℃ | 8.0 | kJ/m² | ISO 179/2C |
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | |||
| -30℃ | 100 | kJ/m² | ISO 179/1eU |
| -30℃ | 75 | kJ/m² | ISO 179/2U |
| 23℃ | 100 | kJ/m² | ISO 179/1eU |
| 23℃ | 67 | kJ/m² | ISO 179/2U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 78 | J/m | ASTM D256 |
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 80 | kJ/m² | |
| 23℃ | 80 | kJ/m² | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 61.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 145 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 141 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 132 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 148 | ℃ | ASTM D1525 11 |
| B50 | 149 | ℃ | ISO 306 |
| B120 | 150 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 123~127℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 4.0E-5 | 1/℃ | ASTM D696 |
| MD：23~80℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-30~30℃ | 4.0E-5 | 1/℃ | ASTM D696 |
| TD：23~80℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 80.0 | ℃ | UL 746 |
| Electrical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.6 mm in oil | 20 | kV/mm | ASTM D149 |
| Relative permittivity | |||
| 50 Hz | 3.20 | ||
| 60 Hz | 3.20 | ||
| 1 MHz | 3.10 | ||
| Dissipation factor | |||
| 50 Hz | 0.020 | ||
| 60 Hz | 0.020 | ||
| 1 MHz | 0.010 | ||
| Compared to the leakage tracing index | 150 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 825 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 38 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 270 to 300 | °C | |
| Barrel middle temperature | 280 to 310 | °C | |
| Barrel front temperature | 290 to 320 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |