| About |
|---|
| 中高流动性聚碳酸酯，用于医疗器械和药物的应用，具有生物相容(ISO10993或USPClass VI). 用于蒸汽、电子束和伽玛灭菌，包含脱模. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Biocompatible |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Rockwell hardness | |||
| M-level | 70 | ASTM D785 | |
| R-level | 118 | ASTM D785 | |
| Taber wear and tear | |||
| CS-17，1kg | 10 | mg/1000cy | ASTM D1044 |
| tensile strength | |||
| Yield, 50 mm/min | 63 | MPa | ISO 527 |
| Fracture, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, 50 mm/min | 6 | % | ISO 527 |
| Fracture, 50 mm/min | 100 | % | ISO 527 |
| Tensile modulus | |||
| 1 mm/min | 2350 | MPa | ISO 527 |
| bending strength | |||
| Yield, 2 mm/min | 90 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 2300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact | |||
| S-shaped | 56 | N.m | ASTM D 1822 |
| Drop hammer impact | |||
| D 3029，23℃ | 173 | N.m | ASTM D3029 |
| Instrument impact energy peak | |||
| 23℃ | 64 | N.m | ASTM D 3763 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 3260 | J/m | ASTM D 4812 |
| 23℃，80*10*3 | NA | kJ/m² | ISO 180/1U |
| -30℃，80*10*3 | NA | kJ/m² | ISO 180/1U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 700 | J/m | ASTM D256 |
| 23℃，80*10*3 | 12 | kJ/m² | ISO 180-1A |
| -30℃，80*10*3 | 10 | kJ/m² | ISO 180-1A |
| 23℃ | NA | kJ/m² | ISO 179/1eU |
| -30℃ | NA | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 80 * 10 * 4, 62mm span | |||
| 23℃ | 35 | kJ/m² | ISO 179/2C |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 154 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 0.45 MPa, 100 mm span | 133 | ℃ | ISO 75/Be |
| 1.8 MPa, 100 mm span | 122 | ℃ | ISO 75/Ae |
| Unannealed, 6.4 mm | |||
| 0.45 MPa | 137 | ℃ | ASTM D 648 |
| 1.8MPa | 129 | ℃ | ASTM D 648 |
| Linear coefficient of thermal expansion | |||
| 23 ℃ to 80 ℃, flowing | 7.E-05 | 1/℃ | ISO 11359-2 |
| -40 ℃ to 95 ℃, flowing | 6.84E-05 | 1/℃ | ASTM E 831 |
| specific heat | 1.25 | J/g-℃ | ASTM C 351 |
| Thermal conductivity coefficient | |||
| 0.19 | W/m/℃ | ASTM C177 | |
| 0.2 | W/m/℃ | ISO 8302 | |
| Vicat Softening Temp | |||
| B50 | 140 | ℃ | ISO 306 |
| B120 | 141 | ℃ | ISO 306 |
| Relative temperature index | |||
| Electrical performance | 130 | ℃ | UL 746B |
| Impact mechanical performance | 130 | ℃ | UL 746B |
| Non mechanical impact performance | 130 | ℃ | UL 746B |
| Ball pressure test | |||
| 125℃±2℃ | PASSES | IEC 60695-10-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.2 | ASTM D792 | |
| Specific volume | 0.83 | cm³/g | ASTM D 792 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| Equilibrium, 100 ℃ | 0.58 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5 – 0.7 | % | Internal Method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 17.5 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，2.16 kg | 16 | cm³/10min | ISO 1133 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2.54 mm | 88 | % | ASTM D1003 |
| Haze | |||
| 2.54 mm | 1 | % | ASTM D1003 |
| Refractive index | 1.586 | ASTM D542 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | >1.E+17 | ohms·cm | ASTM D257 |
| Relative permittivity | |||
| 50-60 Hz | 3.17 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| Dissipation factor | |||
| 50-60 Hz | 0.0009 | ASTM D150 | |
| 1 MHz | 0.01 | ASTM D150 | |
| Dielectric strength | |||
| 3.2 mm in air | 14.9 | kV/mm | ASTM D149 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 50-60 Hz | 2.7 | IEC 60250 | |
| 1 MHz | 2.7 | IEC 60250 | |
| Dissipation factor | |||
| 50-60 Hz | 0.001 | IEC 60250 | |
| 1 MHz | 0.1 | IEC 60250 | |
| Volume resistivity | >1.E+15 | ohms·cm | IEC 60093 |
| Surface resistivity | |||
| — | >1.E+15 | ohms | IEC 60093 |
| Hot wire ignition {PLC} | 2 | PLC Code | UL 746A |
| High voltage arc marking rate {PLC} | 2 | PLC Code | UL 746A |
| High current arc ignition (surface {PLC}) | 1 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 2 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | |||
| LOI | 25 | % | ISO 4589 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3 – 4 | hrs | |
| Drying time (cumulative) | 48 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 280 – 305 | °C | |
| Nozzle temperature | 275 – 300 | °C | |
| Front Section Zone 3 Temperature | 280 – 305 | °C | |
| Temperature in Zone 2 of the middle section | 270 – 295 | °C | |
| Temperature in Zone 1 of the rear section | 260 – 280 | °C | |
| Mold temperature | 70 – 95 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 40 – 70 | rpm | |
| Shoot to cylinder size | 40 – 60 | % | |
| Depth of exhaust groove | 0.025 – 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |